An overwiew on corrosion behavior of steels in factory


Number 2_Vol.5

AUTHORS: H. Demiroren

DOI: 10.32523/ejpfm.2021050203

PAGES: 102 - 115

DATE: 2021-06-22


ABSTRACT

In this study, corrosion behaviors of diffuser unit solution by which raw sugar is produced from minced sugar beets in sugar factories on St-37 low alloy steel and AISI 304, 304L, 316 austenitic stainless steel types were examined. Moreover, influence of heat treatment on corrosion resistance was investigated. Corrosion tests were performed using mass loss method. SEM-EDX, X-rays Diffraction, microhardness and surface hardness analyses of samples were carried out. As a result, it was determined that AISI 304L and 316 steels have better corrosive resistance and heat treatment improves corrosion resistance.


KEYWORDS

industrial factories, corrosion, stainless steel, heat treatment, SEM-EDS analysis


CITED REFERENCES

[1] S. Durmooa et al., Electrochimica Acta 54 (2008) 74-79.

[2] K.H. Lo et al., Wear 392-393 (2017) 159-166.

[3] G. A.Cash, D.P. Schweinsberg, G.A. Hope, Corrosion Science 30(6-7) (1990) 543-554.

[4] N. Karavaizoglu and M. Kabasakaloglu, 3th Corrosion Syposium, Ankara (1998) 199-208.

[5] S.R. Kumar et al., Materials Todays 45 (2021) 1878-1881.

[6] H. Jin et al., Engineering Failure Analysis 122 (2021) 105283.

[7] G.A. Cash et al., Corros. Sci. 33(5) (1992) 751.

[8] G.V. Genie, Sugar Techn. 9 (1982) 119-270.

[9] S. Durmoo et al., Electrochimica Acta 54 (2008) 74-79.

[10] T. Fujii et al., Forces in Mechanics 3 (2021) 100013.

[11] M.S. Anwar et al., Materials Today: Proceedings 44 (2021) 3434-3438.

[12] V. Kumara et al., Materials Today: Proceedings 22(2020) 3347-3352.

[13] S.K. Pradhan et al., Corrosion Science 158 (2019) 108091.

[14] H. Demiroren, J. App. Electrochem. 39 (2009) 39:761-767.

[15] J. Paro et al., J. Mater. Process. Technol. 14 (2001) 119-130.

[16] 16 L.P. Karjalainen et al., Steel Res. Int. 79 (2016) 404-412.

[17] E. Zumelzu et al., J. Mater. Process. Technol 16 (2002) 250-255.

[18] K. Karacif and B. Inem, J. Fac. Eng. Archit. 16(1) (2001) 1-8.

[19] P. Refait et al., Corrosion Science 71 (2013) 32-36.

[20] R. Lackner et al., BHM 158(9) (2013) 364-370.

[21] M. Soleimani et al., Mater. Res. Express 7 (2020) 016522.

[22] J.R.S. Moreno and C.E.S. Junior, American Journal of Materials Science 4(5) (2014) 185-189.


Download file Open file